    TZS? Zirconium Silciate grinding beads

    Page view:
    Name

    TZS? Zirconium Silciate grinding beads

    沒有此類產品
    Product description

    Tecera International

    Zirconium Silciate grinding beads

    Application:

    Type

    Application

    TZS320?

    1. Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and    other minerals;
    2.Metallic minerals like copper, silver, nickel, gold, zinc etc;
    3. White pigments, coatings, paints, inks etc;
    4.Recommend to be used in stirred mill and ball mill.

    TZS360?

    1. Non-metallic minerals like Zirconium Silicate, Calcium Carbonate, kaolin clay;
    2. Ceramic glazes and frits;
    3. Coatings, paints, inks etc;
    4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
    5. Recommend to be used in stirred mill and ball mill.

    TZS400?

    1. Non-metallic minerals like Zirconium Silicate,GCC, kaolin clay;
    2. Engineering Ceramics.
    3. Coatings, paints, inks etc;
    4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
    5. Metal finishing and polishing.

    TZS420?

    1.Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and    other minerals;
    2. Dielectric materials, piezoelectric materials, capacitor;
    3. Ceramic glazes and frits;
    4. Coatings, paints, inks etc;
    5. Metallic minerals like copper, silver, nickel, gold, zinc etc;
    6. Recommend to be used in stirred mill and ball mill.

    Specification  

    Specification

    TZS 320?

     TZS360?

    TZS400?  

    TZS420?

    Chemical
    composition

    ZrO2 Al2O3   SiO2  
    Other

    ZrO2   Al2O3   SiO2  
    Other

    ZrO2   Al2O3   SiO2 
    Other

    ZrO2   Al2O3   SiO2 
    Other

    Density

    >3.25

    3.60~3.70

    >4.0

     4.20min

    Packing 
    Density

    >1.85


    2.20~2.35

    >2.35

    2.85min

    Hardness
    (Mohs)

    8  

    8  

    > 8

    8min

    Roundness

    >90%

    >90%

    >90%

    >90%

    Size

    0.2 ~ 12mm  ,

    0.2 ~ 12mm,

    0.4 ~ 13mm,.

    0.2 ~ 12mm,

    Color

    White

    White

    off-white

    White

     

    ■Packaging:

    25kg net in PP-bag or big bag of 500 or 1000kg net. 20-24MT/20'FCL.

    ■Key benefits:

    ·Very High grinding efficiency for superfine grinding.

    ·Fine chemical stability & contamination-free to the grinded material.

    ·Extremely low wear rate .

    ·Excellent combination of toughness and hardness .

    ·Technical support provided to optimize milling conditions .

    Wear Loss Testing

    Grinding Beads

    Size
    (mm)

    Beads loading
    quantity/g

    Weight of beading after grinding/g

    Wear Loss/g

      Wear Loss 
    Rate /%

    Alumina Grinding Beas
    (China)

    8

    500

    498.6

    1.4

    0.28%

    TZS400 ceramic beads

    8-10

    500

    499.7

    0.3

    0.06%

    Testing Method:Ceramic beads loading quantity 500g, water loading quantity150g,grinding time 1 hour,volume of jar mill : 500ml.

    ■Conclusion: 

    The wear loss rate of alumina ceramic beads is about 4.6 times higher than TZS400 zirconium silicate grinding beads.

     
    Corresponding parameter set not found, please add it in property template of background